1. The heat treatment quality of the aluminum extrusion die directly affects the service life of the extrusion die. The die is hardened by "+" tempering several times to reach the hardness requirements. Quenching is to improve the hardness of the die, and multiple tempering is to improve the toughness of the die and stabilize the internal organization. The hardness value of the die heat treatment is specified as follows: large aluminum extrusion die (F>500 mm), HRC45-48; Keskmine vorm (F300 ~ 500 mm), HRC47-50; Väike ekstrusioonivorm (F<300mm), hrc48-51;="" test="" three="" points="" on="" the="" same="" plane="" of="" a="" set="" of="" molds,="" and="" the="" hardness="" values="" of="" each="" point="" should="" be="" qualified="" within="" the="" specified="">
2. Erilist tähelepanu tuleks pöörata ekstrusioonivormi kuumtöötlusprotsessis järgmistele punktidele:
a. Kõrge temperatuuriga sektsiooni kuumutamiskiirus peaks olema kiire ja hoidmisaeg ei tohiks olla liiga pikk, et vältida ekstrusioonvormi ülepõlemist või ülekuumenemist. Ülekuumenenud -- jämedad terad, ülepõlevad -- madala sulamistemperatuuriga elemendid ja inklusioon lahustuvad;
b. Karastage alumiiniumist ekstrusioonivormi õigeaegselt pärast kustutamist, et vältida pragude tekkimist;
c. Kui pärast kuumtöötlemist leitakse, et ekstrusioonivormi kõvadus on ebapiisav või ebaühtlane, tuleb see lõõmutada ja kuumtöötlus uuesti läbi viia vastavalt protsessile (kui kõvaduse väärtus on väiksem kui HRC35, lõõmutamist ei toimu lubatud ja kuumtöötlus viiakse läbi otse);
d. Suurte alumiiniumist ekstrusioonvormide või keeruka õõnsusega viimistletud stantside jaoks tuleks lisada pinge vähendamise ja karastamise protsess (elektrilise töötlemise ja töötluspinge kõrvaldamiseks, st termilise ja organisatsioonilise pinge kõrvaldamiseks);
e. Kas stantsikustutusõli temperatuur peaks olema? 100 kraadi, et tagada kustutusefekt.